CHEMICAL COMPOSITION ( IN PERCENTAGE ) | ||||||||||
Grade
|
C (Max)
|
Mn (Max)
|
P (Max)
|
S (Max)
|
If (Max)
|
Cr
|
Nor
|
Mo
|
Nitrogen (Max)
|
Cu/ Others
|
301
|
0.15
|
2.00
|
0.045
|
0.030
|
1.00
|
16.00 - 18.00
|
6.00 - 8.00
|
-
|
0.10
|
-
|
304
|
0.08
|
2.00
|
0.045
|
0.030
|
0.75
|
18.00 - 20.00
|
8.00- 10.50
|
-
|
0.10
|
-
|
304L
|
0.030
|
2.00
|
0.045
|
0.030
|
0.75
|
18.00 - 20.00
|
8.00- 12.00
|
-
|
0.10
|
-
|
310S
|
0.08
|
2.00
|
0.045
|
0.030
|
1.50
|
24.00- 26.00
|
19.00 - 22.00
|
-
|
-
|
-
|
316
|
0.08
|
2.00
|
0.045
|
0.030
|
0.75
|
16.00 - 18.00
|
10.00 - 14.00
|
2.00 - 3.00
|
0.10
|
-
|
316L
|
0.030
|
2.00
|
0.045
|
0.030
|
0.75
|
16.00 - 18.00
|
10.00 - 14.00
|
2.00 - 3.00
|
0.10
|
-
|
317
|
0.08
|
2.00
|
0.045
|
0.030
|
0.75
|
18.00 - 20.00
|
11.00 - 14.00
|
3.00 - 4.00
|
0.10
|
-
|
317L
|
0.030
|
2.00
|
0.045
|
0.030
|
0.75
|
18.00 - 20.00
|
11.00 - 15.00
|
3.00 - 4.00
|
0.10
|
-
|
321
|
0.08
|
2.00
|
0.045
|
0.030
|
0.75
|
17.00 - 19.00
|
9.00 - 12.00
|
-
|
0.10
|
Ti5 ( C + N ) Min or
0.70 max
|
347
|
0.08
|
2.00
|
0.045
|
0.030
|
0.75
|
17.00 - 19.00
|
9.00 - 13.00
|
-
|
-
|
Cb= 10x ( C Min ) or
1.00 Max
|
409
|
0.08
|
1.00
|
0.040
|
0.010
|
1.00
|
10.50 - 11.75
|
0.50
|
-
|
-
|
Ti= 6x (C+N) Min or
0.70 Max
|
409M
|
0.03
|
0.81.2
|
0.030
|
0.030
|
0.40.75
|
11.00- 12.00
|
1.5 max.
|
-
|
-
|
Ti= 6x (C) Min or 0.70
Max
|
410S
|
0.08
|
1.00
|
0.040
|
0.030
|
1.00
|
11.50- 13.50
|
0.60
|
-
|
-
|
-
|
410
|
0.15
|
1.00
|
0.040
|
0.030
|
1.00
|
11.50- 13.50
|
0.75
|
-
|
-
|
-
|
420
|
0.35
|
0.50
|
0.035
|
0.015
|
0.50
|
12.00 - 13.00
|
0.20.3
|
-
|
-
|
-
|
430
|
0.12
|
1.00
|
0.040
|
0.030
|
1.00
|
16.00 - 18.00
|
0.75
|
-
|
-
|
-
|
JSL AUS
|
0.08
|
7.08.0
|
0.070
|
0.030
|
0.75
|
15.50 - 16.50
|
4.25 - 4.75
|
-
|
-
|
0.9 - 1.10
|
JS- 203
|
0.08
|
9.2510.25
|
0.070
|
0.030
|
0.75
|
14.25 - 15.25
|
2.25 - 2.75
|
-
|
-
|
1.60- 2.0
|
301M
|
0.10
|
4.55.5
|
0.060
|
0.030
|
0.75
|
14.50 - 15.50
|
6.0 - 7.0
|
-
|
-
|
1.70- 1.90
|
* Thickness of 1.27mm & below will have elongation of 20% min. |